Tšobotsi ea mantlha ea Bimetal Bimetal e fetoha ka mocheso le Deflices, lisebelisoa li sebelisetsoa tsamaiso ea litlolo.
Lebenkele la lebenkele | 5j1480 | |
Ka Brand | 528 | |
Sebopeho sa Composite aloybrand | Katoloso ea Matla a phahameng | Ni22cr3 |
Lala ea Bohareng | --- | |
Katoloso e tlase ea ho eketseha | Ni36 |
Sebopeho sa lik'hemik'hale
Lebenkele la lebenkele | Ni | Cr | Fe | Co | Cu | Zn | Mn | Si | C | S | P |
≤ | |||||||||||
Ni36 | 35.0 ~ 37.0 | - | tumello | - | - | - | ≤0.6 | ≤0.3 | 0.05 | 0.02 | 0.02 |
Ni22cr3 | 21.0 ~ 23.0 | 2.0 ~ 4.0 | tumello | - | - | - | 0.3 ~ 0,6 | 0.15 ~ 0.3 | 0.25 ~ 0.35 | 0.02 | 0.02 |
Ts'ebetso
Ho feta ho khumama k (20 ~ 135ºC) | Mocheso oa mocheso F / (Greenhouse ~ 130 ºC) | TLHOKOMELISO | Mocheso oa Lineare / º- | E lumella tšebeliso ea mocheso / ºC | Letsoalo (g / cm ka mor'a) | |||
Boleng ba lebitso | Ho kheloha ho lumelletsoeng | Melao e tloaelehileng | Ho kheloha ho lumelletsoeng | |||||
Boemo ba 1 | Boemo ba 2 | |||||||
14.3 | ± 5% | ± 7% | 26.2% ± 5% | 0.8 | ± 5% | -20 ~ 180 | -70 ~ 350 | 8.2 |
Modululus oa Elasticity E / GPA | Hardness (Hv) | Matla a tšepe Mpa | Lumella khatello ea maikutlo mpa | ||
Katoloso ea Matla a phahameng | Katoloso e tlase ea ho eketseha | bonyane | e kholo | ||
147 ~ 177 | 270 ~ 340 | 200 ~ 255 | 785 ~ 883 | 196 | 343 |