Copper Nickel CuNi23 Stranded Resistance Wire bakeng sa ho futhumatsa

Tlhaloso e Khutšoanyane:

Copper Nickel Alloy e entsoe haholo ka koporo le nickel. Koporo le nickel li ka qhibiliha hammoho ho sa tsotellehe hore na ke peresente e kae. Ka tloaelo, resistivity ea CuNi alloy e tla ba holimo haeba litaba tsa Nickel li le kholo ho feta Copper content. Ho tloha CuNi6 ho ea CuNi44, resistivity e tloha 0.03μΩm ho 0.49μΩm. Sena se tla thusa mohanyetsi ho khetha terata e loketseng ea alloy.


  • Lebitso la sehlahisoa:Motsoako oa koporo oa nickel
  • Resistivity:0.3
  • Boholo:0.05-2.5 limilimithara
  • Tekano:8.9g/cm3
  • Bokaholimo:E kganyang
  • mohlala:amohela taelo e nyane
  • Tšimoloho:Shanghai, China
  • Lintlha tsa Sehlahisoa

    LBH

    Li-tag tsa Sehlahisoa

    Tloaelehilengtlhamo%

    Nickel 23 Manganese 0.5
    Koporo Bal.

     

    E tloaelehilengThepa ea mechine(1.0mm)

    Ho hlahisa matla Matla a tšepe Elongation
    Mpa Mpa %
    170 350 25

     

    E tloaelehilengLintho tsa 'mele

    Boima ba 'mele (g/cm3) 8.9
    Ho hanyetsa motlakase ho 20ºC (Ωmm2/m) 0.30
    Thempereichara ea ho hanyetsa (20ºC~600ºC)X10-5/ºC <16
    Conductivity coefficient ho 20ºC (WmK) 33
    EMF vs Cu(μV/ºC )(0~100ºC ) -34

     

    Coefficient ea katoloso ea mocheso
    Mocheso Katoloso ea Mocheso x10-6/K
    20 ºC-400ºC 17.5

     

    Matla a khethehileng a mocheso
    Mocheso 20ºC
    J/gK 0.380

     

    Sebaka se qhibilihang (ºC) 1150
    Mocheso o phahameng o sa khaotseng oa ho sebetsa moeeng (ºC) 300
    Lintho tsa Magnetic e seng ea makenete

    Ts'ebetso ea ho hanyetsa kutu

    Alloys Ho sebetsa Sebakeng sa 20ºC E sebetsa ka mocheso o phahameng oa 200ºC
    Moea le oksijene li na le
    likhase
    likhase tse nang le naetrojene likhase tse nang le sebabole
    phokotso ya oxidability
    likhase tse nang le sebabole
    phokotso
    carburization
    Motsoako oa 180 molemo kakaretso kakaretso kakaretso mpe molemo