FeCrAl 135 Alloy Electric Resistance Heating Wire Ocr25al5 Ocr23al5 Ocr21al6 bakeng sa Likhoeli tsa Heater
FeCrAl135 ke motsoako oa ferritic iron-chromium-aluminium alloy (FeCrAl alloy) bakeng sa tšebeliso ea mocheso ho fihlela ho 1300 ° C (2370 ° F). The alloy e khetholloa ka ho hanyetsa ho phahameng le ho hanyetsa oxidation e ntle.
FeCrAl135 e sebelisoa lisebelisoa tsa lapeng le libopi tsa indasteri. Lisebelisoa tse tloaelehileng ka har'a lisebelisoa tsa lapeng li kenyelletsa likarolo tsa tšepe tse kentsoeng ka tšepe bakeng sa lisebelisoa tsa ho hlatsoa lijana, lisebelisoa tse kentsoeng ka har'a li-ceramics bakeng sa li-heaters tsa pane, likarolo tsa cartridge ka har'a tšepe, lithapo tse futhumatsang le licheso tsa thapo linthong tse defrosting le deicing, likarolo tsa mica tse sebelisoang ka tšepe, lihitara tsa quartz bakeng sa ho futhumatsa sebaka. , li-dryer tsa infrared tsa indasteri, ka li-coil tse holim'a fiber ea ceramic e bōpiloeng bakeng sa lipoleiti tse belang tse nang le li-hobs tsa ceramic, ka li-coil tse insulated bakeng sa li-heaters tsa panels, ka likarolo tse emisitsoeng tsa coil bakeng sa licheso tsa moea tse omisitsoeng liaparo.
Lits'ebetsong tsa indasteri, FeCrAl135 e sebelisoa, ho etsa mohlala, ho liteishene tsa sebōpi, likarolo tsa porcupine bakeng sa ho futhumatsa moea, le linthong tse futhumatsang tsa sebōpi.
MOTS'EOA CHEMEKE
C% | Si% | Mn% | Cr% | Al% | Fe% | |
Moqapi ka lebitso | 5.3 | Bal. | ||||
Min | - | - | - | 23.0 | - | |
Max | 0.05 | 0.5 | 0.45 | 25.0 | - |
LITŠOANTŠISO MOCHEFE
Botenya | Ho hlahisa matla | Matla a tšepe | Elongation | Ho thatafala |
R0.2 | Rm | A | ||
mm | Mpa | MPa | % | Hv |
2.0 | 450 | 650 | 18 | 200 |
LITŠOANTŠISO MONATE
Boima ba g/cm3 | 7.15 |
Ho hanyetsa motlakase ho 20°C Ω mm / m | 1.35 |
Boholo ba mocheso oa tšebeliso °C | 1300 |
Sebaka se qhibilihang °C | 1500 |
Thepa ea Magnetic | Magnetic |
MOCHESO NTHO E TS'OALANG
Mocheso °C | 200 | 300 | 400 | 500 | 600 | 700 | 800 | 900 | 1000 | 1100 | 1200 | 1300 |
Ct | 1.00 | 1.01 | 1.01 | 1.02 | 1.03 | 1.03 | 1.04 | 1.04 | 1.04 | 1.05 | 1.05 | 1.05 |