Permalloy E11c Ni79Mo4 79HM Soft Magnetic Alloy Wire

Tlhaloso e Khutšoanyane:


Permalloy 80 ke motsoako oa nickel, tšepe le molybdenum.Ke motsoako o bonolo oa makenete o nang le matla a matla a khoheli a phahameng haholo.Alloy e na le coercivity e tlase, haufi le zero magnetostriction, le bohlokoa ba anisotropic magnetoresistance.The magnetostriction e tlase e bohlokoa bakeng sa lits'ebetso tsa indasteri,

moo likhatello tse feto-fetohang lifiliming tse tšesaane li neng li ka baka phapang e mpe haholo ea litšobotsi tsa makenete.


  • Nomoro ea mohlala:Permalloy
  • Resistivity:0.55
  • Elongation (≥ %):15-25
  • Kereiti:E11C
  • Ke:78.5-80.0%
  • Sebopeho:Pheheletso e Phahameng ea Pele
  • Tšimoloho:China
  • Lintlha tsa Sehlahisoa

    LBH

    Li-tag tsa Sehlahisoa

    Paramethara

    TABLE EA 1 Tlhokahalo ea Lik'hemik'hale

    Element C≤ P≤ S≤ Mong Si Ho ≤ Mo Ni Fe
    Moetso% 0.03 0.02 0.02 0.6-1.1 0.3-0.5 0.20 3.8-4.1 78.5-80.0 Mesala

    Lintlha:

    Sebopeho le boholo ba li-alloys li lumellana le GBn198-88

    TABLE EA 2 Tlhokahalo ea 'Mele

    Thepa Resisitivity(μΩM) Desinty(g/cm3) Curie Point.C Matla a phahameng a magneto-striction coeffientλθ/10-6
    Boleng 0.55 8.6 450 2

    TABLE 3 AC Magnetic Properties for Strip(Boleng ba metsotso)

    Botenya Tlhōrō ea matla a matla a khoheli ke 0.1A/m, Tlas'a maqhubu a fapaneng a matla a matla a khoheli μm/(mH/m)
    60Hz 400Hz 1KHz 10KHz
    0.02 17.5 12.5
    0.05 18.8 9.4
    0.10 22.5 15
    0.20 12.5 7.5
    0.35 25 8.8

    TABLE 4 Coefficient of Linear Katoloso ka Mocheso o fapaneng/(x10-6)

    Temp 20-100°C 20-200ºC 20-300ºC 20-400ºC 20-500ºC 20-600ºC 20-700ºC
    Boleng 1.3-10.8 10.9-11.2 14.4-12.9 11.9-12.5 12.3-13.2 12.7-13.4 13.1-13.6

    TABLE 5 Tlhokahalo ea Magnetic (Mohala o batang o kolohang)

    Sehlopha sa I

    (δ&D)/mm μ0.08/(mHm)≥ μm(mHm)≥ Bs/T≥ Hc(A/M)≤
    0.005 12.5 44.0 0.75 6.4
    0.01 17.5 87.5 0.75 4.8
    0.02-0.04 20.0 112.5 0.75 4.0
    0.05-0.09 22.5 137.5 0.75 2.8
    0.10-0.19 25.0 162.5 0.75 2.0
    0.20-0.34 28.0 225.0 0.75 1.6
    0.35-1.00 30.0 250.0 0.75 1.2
    1.10-2,50 27.5 225.0 0.75 1.6
    2.50-3.00 26.3 187.5 0.75 2.0

    Sehlopha sa II

    (δ&D)/mm μ0.08/(mHm)≥ μm(mHm)≥ Bs/T≥ Hc(A/M)≤
    0.02-0.04 22.5 125.0 0.75 2.4
    0.05-0.09 25.0 150.0 0.75 2.0
    0.10-0.19 27.5 187.5 0.75 1.6
    0.20-0.34 31.3 250.0 0.75 1.2
    0.35 32.5 275.0 0.75 0.79

    Sehlopha sa III

    (δ&D)/mm μ0.08/(mHm)≥ μm(mHm)≥ Bs/T≥ Hc(A/M)≤
    0.01 25.0 150.0 0.73 2.4
    0.02-0.04 31.0 190.0 0.73 1.6
    0.05-0.09 38.0 250.0 0.73 1.2
    0.10-0.19 38.0 250.0 0.73 1.2
    0.20-0.34 38.0 280.0 0.73 1.0
    0.35 44.0 310.0 0.73 1.0

    Hot Rolling(forging) Flastspring

    (δ&D)/mm μ0.08/(mHm)≥ μm(mHm)≥ Bs/T≥ Hc(A/M)≤
    3-22 25.0 125 0.75 2.4

    Hot Rolling (Forging)Bar

    (δ&D)/mm μ0.08/(mHm)≥ μm(mHm)≥ Bs/T≥ Hc(A/M)≤
    8-100 25.0 125.0 0.75 2.4