Silver Copper Wire AG50cu50 Silver Alloy Wire

Tlhaloso e Khutšoanyane:

AG50Cu50, Sebaka se qhibilihang ke 779-850 C

Boima: 0.1mm -3.0mm

AG72Cu28, Sebaka se qhibilihang ke 779-779 C

Boima: 0.08mm-6.0mm

AG45Cu30Zn25, Sebaka sa ho kopana ke 660-725 C

Nomoro ea mohlala:Ag50Cu50

Boholo:0.02mm Min.

bokaholimo:E kganyang

maemo:GB/ASTM

Re romelle lengolo-tsoibila

Lintlha tsa Sehlahisoa

LBH

Li-tag tsa Sehlahisoa

Diamater: 0.1mm-6.0mmKopo : e loketse tšepe ea brazing, tšepe e sa hloekang, li-alloys tsa koporo, alloy ea nickel joalo-joalo.
Pakete: 1Kg / spool;1Kg/polybag;2Kg/polybag;Ring, peista le flux coated A fumaneha;Lebokose kapa ho ea ka kopo.

Silevera Alloy ea Brazing	Sebopeho sa Lik'hemik'hale (%)	Solidus	Liquidus	Tlhaloso (mm)	Litekanyetso
BAg10CuZn (HL301)	Ag:9.0-11.0 Ka:52.0-54.0 Zn: 35.0-39.0 Tse ling: Max0.15	815ºC	850ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	Khoebo
BAg15CuZn	Ag:14.0-16.0 Ka:46.0-48.0 Zn: 36.0-40.0 Tse ling: Max0.15	750ºC	830ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	Khoebo
BAg18CuZn	Ag,Ku,Zn	700ºC	815ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	Khoebo
BAg20CuZn	Ag:19.0-21.0 Ka:43.0-45.0 Zn:34.0-38.0 Tse ling: Max0.15	690ºC	810ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 EN1044:1999 AG206
BAg25CuZn (HL302)	Ag:24.0-26.0 Ka:39.0-41.0 Zn:33.0-37.0 Tse ling: Max0.15	700ºC	790ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 EN1044:1999 AG205 ISO 17672:2010 Ag225
BAg30CuZn	Ag:29.0-31.0 Ka:37.0-39.0 Zn:30.0-34.0 Tse ling: Max0.15	680ºC	765ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 AWS A5.8 BAg-20 EN1044:1999 AG204 ISO 17672:2010 Ag230
BAg35CuZn	Ag:34.0-36.0 Ka:31.0-33.0 Zn:31.0-35.0 Tse ling: Max0.15	685ºC	775ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 AWS A5.8 BAg-35
BAg44CuZn	Ag:43.0-45.0 Ka:29.0-31.0 Zn: 24.0-28.0 Tse ling: Max0.15	675ºC	735ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 EN1044:1999 AG203 ISO 17672:2010 Ag244
BAg45CuZn (HL303)	Ag:44.0-46.0 Ka:29.0-31.0 Zn: 24.0-27.0 Tse ling: Max0.15	665ºC	745ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 AWS A5.8 BAg-5
BAg50CuZn (HL304)	Ag:49.0-51.0 Ka:33.0-35.0 Zn: 14.0-18.0 Tse ling: Max0.15	690ºC	775ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 AWS A5.8 MOKHOA-6
BAg60CuZn	Ag:59.0-61.0 Ka:25.0-27.0 Zn: 12.0-16.0 Tse ling: Max0.15	695ºC	730ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 EN1044:1999 AG202
BAg65CuZn (HL306)	Ag:64.0-66.0 Ka: 19.0-21.0 Zn: 13.0-17.0 Tse ling: Max0.15	670ºC	720ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 AWS A5.8 BAK-9
BAG70CuZn (HL307)	Ag:6.0-7.0 Ka: 19.0-21.0 Zn:8.0-12.0 Tse ling: Max0.15	690ºC	740ºC	Thupa/Mohala/Ring/Flat ≥φ0.2 Leqhala/Lebanta/Foil /preforming Botenya≥0.05 2.0≤Bophara≤100	GB/T10046-2008 AWS A5.8 BAg-10