4J36 (Invar) e sebelisoa moo ho hlokahalang botsitso bo phahameng, joalo ka lisebelisoa tse nepahetseng, lioache, litekanyo tsa ho reketla ha litšisinyeho tsa lefatše, liforeimi tsa maske tsa moriti oa thelevishene, li-valve tsa lienjene, le lioache tse thibelang makenete.Ha ho etsoa tlhahlobo ea mobu, ha ho etsoa boemo ba boemo bo phahameng ka ho fetisisa (ho nepahala) ho etsoa, ho sebelisoa basebetsi ba Level (leveling rod)Invar, ho e-na le lehong, fiberglass, kapa litšepe tse ling.Li-invar struts li ne li sebelisoa lipiston tse ling ho fokotsa katoloso ea tsona ea mocheso ka har'a lisilindara tsa tsona.
4J36 sebelisa oxyacetylene welding, motlakase arc welding, welding le mekhoa e meng.Kaha coefficient ea katoloso le metsoako ea lik'hemik'hale tsa motsoako e amana e lokela ho qojoa ka lebaka la tjheseletsa bakang phetoho motsoako motsoako, ho molemo ho sebelisa Argon arc tjheseletsa tjheseletsa filler tšepe ka ho khetheha e na le 0.5% ho 1.5% titanium, e le hore a fokotsa weld porosity le petsoha.
Sebopeho se tlwaelehileng%
Ni | 35~37.0 | Fe | Bal. | Co | - | Si | ≤0.3 |
Mo | - | Cu | - | Cr | - | Mn | 0.2 ~ 0.6 |
C | ≤0.05 | P | ≤0.02 | S | ≤0.02 |
Coefficient ea katoloso
θ/ºC | α1/10-6ºC-1 | θ/ºC | α1/10-6ºC-1 |
20 ~ 60 | 1.8 | 20-250 | 3.6 |
Lilemo tse 20-40 | 1.8 | 20-300 | 5.2 |
20 ~ 20 | 1.6 | 20 ~ 350 | 6.5 |
20~-0 | 1.6 | 20-400 | 7.8 |
20-50 | 1.1 | 20-450 | 8.9 |
20 ~ 100 | 1.4 | 20 ~ 500 | 9.7 |
20 ~ 150 | 1.9 | 20 ~ 550 | 10.4 |
20 ~ 200 | 2.5 | 20-600 | 11.0 |
Boima ba 'mele (g/cm3) | 8.1 |
Ho hanyetsa motlakase ho 20ºC(OMmm2/m) | 0.78 |
Thempereichara ea ho hanyetsa (20ºC~200ºC)X10-6/ºC | 3.7~3.9 |
Thermal conductivity, λ/ W/(m*ºC) | 11 |
Curie ntlha Tc/ ºC | 230 |
Elastic Modulus, E/Gpa | 144 |
Mokhoa oa phekolo ea mocheso | |
Annealing bakeng sa ho imolla khatello ea maikutlo | E futhumala ho 530 ~ 550ºC 'me u tšoare 1 ~ 2 h.Hatsela |
annealing | E le ho felisa ho thatafala, e leng ho hlahisa ka mokhoa o batang, o batang oa ho taka.Anealing e hloka ho futhumatsoa ho 830 ~ 880ºC ka vacuum, tšoara 30 min. |
Mokhoa oa ho tsitsisa |
|
Mehato ya tlhokomelo |
|
Tloaelehileng Mechanical thepa
Matla a tšepe | Elongation |
Mpa | % |
641 | 14 |
689 | 9 |
731 | 8 |
Mocheso oa mocheso oa resistivity
Boemo ba mocheso, ºC | 20-50 | 20 ~ 100 | 20 ~ 200 | 20-300 | 20-400 |
aR/ 103 *ºC | 1.8 | 1.7 | 1.4 | 1.2 | 1.0 |